耐刮花亚克力PMMA 韩国LG HI835M 进口原装 可开税票
PMMA/HI835M/LG化学HI835M物性表
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 水吸收性 | 24h | ASTM D-570 | 0.4 | % |
| 物理性能 | 反射指数 | ASTM D-542 | 1.49 | ||
| 透明性 | 3.2mm | ASTM D-1003 | 92 | % | |
| 比重 | ASTM D-792 | 1.17 | |||
| 机械性能 | 弯曲模数 | ASTM D-790 | 24100 | Kg/cm2 | |
| 拉力 | ASTM D-638 | 520 | Kg/cm2 | ||
| 洛氏硬度 | M-Scale | ASTM D-785 | 70 | ||
| 弯曲强度 | ASTM D-790 | 955 | Kg/cm2 | ||
| 冲击强度 | Izod Notched | ASTM D-256 | 3.5 | kg·cm/cm2 | |
| 延伸率 | ASTM D-638 | 66 | % | ||
| 电气性能 | 介电定数 | 60Hz | ASTM D-150 | 3.5 | |
| 功率系数 | 60Hz | ASTM D-150 | 0.04 | ||
| 介电强度 | 4KV/S | ASTM D-149 | 15 | KV/mm | |
| 抗体积系数 | ASTM D-257 | >10 | Ω.cm | ||
| 热性能 | 模缩系数 | ASTM D995-51 | 0.4-0.8 | % | |
| 热变形温度 | 18.6kg | ASTM D-648 | 93 | °C | |
| 比热 | 0.35 | cal/g/°C | |||
| 绵性膨胀系数 | ASTM D-696 | 6×10-5 | cm/cm/°C | ||
| 热传导 | ASTM D-177 | 5×10-4 | cal/seccm·°C/cm | ||
| 流动指数 | 230°C,3.8kg | ASTM D-1238 | 3 | g/10min | |
| 维卡软化点 | 1kg | ASTM D-1525 | 103 | °C | |
| 燃烧度 | UL94 | HB | 1/8",1/16" | ||
PMMA
透明性：PMMA是无定形高聚物，其内部分子的排列方式不致干扰进入它的光线在各个部分通过时的速度，因而能使光线都以相同速度前进(即均一的折光指数)，根本不会使光线四面分散互相干扰。所以PMMA具有优良的光学性能，高度的透光率(90～92%，和波长有关)。
表面极光滑的片或棒材，在弯曲到一定限度内也能将从一端射入的光线全部在其内部反射前进， 从另一端射出，就好象水在管子里流过一样(一定的弯曲度是指弯曲后的位置和原来位置所成的角度，不能超过42°;弯曲呈弧形时，弧形半径必须大于棒直径或片材厚度的3倍)。但当其表面某部分磨毛时，光线就可从这里逸出而显示出光亮。可以利用这种特性来制造边缘发光装置、外科医疗器具等。